There is now a CONTENT FREEZE for Mercury while we switch to a new platform. It began on Friday, March 10 at 6pm and will end on Wednesday, March 15 at noon. No new content can be created during this time, but all material in the system as of the beginning of the freeze will be migrated to the new platform, including users and groups. Functionally the new site is identical to the old one. webteam@gatech.edu
*********************************
THE SCHOOL OF MATERIALS SCIENCE AND ENGINEERING
GEORGIA INSTITUTE OF TECHNOLOGY
Under the provisions of the regulations for the degree
MASTER OF SCIENCE
on Wednesday, April 13, 2022
2:30 PM
In Love 109
& via
BlueJeans Video Conferencing
https://bluejeans.com/2518603373
will be held the
MASTER’S THESIS DEFENSE
for
Benjamin Jean
"Controlling Inorganic Loading in Polymer of Intrinsic Microporosity 1 with Vapor Phase Infiltration Vapor Pressure, Exposure Time, and Precursor Chemistry"
Committee Members:
Prof. Mark Losego, Advisor, MSE
Prof. Ryan Lively, ChBE
Prof. Faisal Alamgir, MSE
Abstract:
Vapor phase infiltration (VPI) is a post-polymerization modification method for infusing inorganic clusters into a polymer to create organic-inorganic hybrid materials with properties unique from the parent polymer. The properties of these hybrid materials can vary with the amount of VPI generated inorganic loading. However, because mass uptake during VPI consists of both entrapped species as well as species that are dissolved within the polymer, the relationship between VPI processing conditions and the VPI mass uptake is still not fully understood. In this thesis, the effects of precursor-polymer compatibility as well as VPI dose pressure and exposure time on the final VPI generated inorganic loading is explored using the technologically relevant membrane material polymer of intrinsic microporosity 1 (PIM-1). To understand the differences in inorganic loading, experimentally observed variations in precursor chemistry, are compared with density functional theory (DFT) calculated precursor-to-polymer binding energies. Inorganic loading is found to correlate with higher binding energy complexes. Moreover, inorganic loading can be controlled with both precursor vapor pressure and exposure time at sufficiently low dose pressures and infiltration times (i.e., before saturation). However, inorganic loading appears to saturate for this system when the polymer’s functional groups become fully populated with bound VPI precursors. This means that at higher pressures, the inorganic loading is not necessarily increased, however the kinetics get faster. These experimental results can be understood with the use of a recently developed reaction-diffusion model for VPI. Critical to applying this model to these post-deposition measurements is re-normalizing the reaction-diffusion model calculated mass loading to the total number of functional groups in the polymer. Lastly, this thesis provides a framework to describe VPI mass uptake kinetics using purely ex-situ measurement techniques.