There is now a CONTENT FREEZE for Mercury while we switch to a new platform. It began on Friday, March 10 at 6pm and will end on Wednesday, March 15 at noon. No new content can be created during this time, but all material in the system as of the beginning of the freeze will be migrated to the new platform, including users and groups. Functionally the new site is identical to the old one. webteam@gatech.edu
*********************************
THE SCHOOL OF MATERIALS SCIENCE AND ENGINEERING
GEORGIA INSTITUTE OF TECHNOLOGY
Under the provisions of the regulations for the degree
DOCTOR OF PHILOSOPHY
on Thursday, July 18, 2019
10:00 AM
in LOVE 295
will be held the
DISSERTATION DEFENSE
for
Yoon Joo Na
"Using Strain Field Mining to Reveal the Spatial Distributions of Tensile, Fatigue, and Fracture Damage Accumulation in Paper"
Committee Members:
Prof. Christopher Muhlstein, Advisor, MSE
Prof. Arun Gokhale, MSE
Prof. Surya Kalidindi, ME
Prof. Meisha Shofner, MSE
Prof. Preet Singh, MSE
Abstract:
The most common nonwoven fiber composite material, paper, has a porous, heterogeneous fiber network structure and complicated mechanical properties. The mechanical properties of commercial, machine made papers are orthotropic and are sensitive to loading rate, moisture content, and temperature. Thus, defining the constitutive relationship of paper has remained as a challenge due to the stochastic nature of the structure and countless variables that affect the mechanics of paper. Moreover, the technology to non-destructively characterize the three-dimensional network topography at the fiber length scale is not readily available. This presents a critical barrier to establishing the structure-property relationships of paper. Here, I approached the problem with a fundamentally different strategy and used the structure of the strain fields as a proxy for the network topography. The strain fields of paper from tensile, fatigue, tearing experiments revealed new information about each damage mechanisms. During the tensile deformation, the interplay between the axial and the transverse motions in the fiber network resulted in specimen-orientation-dependent (MD and CD) parameters such as Poisson's ratio, hot spot length scales, and the degree of nonaffinity, D. These metrics were direct manifestation of the anisotropic fiber network in paper. Next, I used strain field mining to track the fatigue crack lengths and quantified crack growth rates during cyclic and constant loading conditions. The fracture profiles and the crack growth rates revealed that there was a unique fatigue damage mechanism in paper which induced the fiber fracture rather than the fiber pull-out. Moreover, I found that the pre-applied creep damage in paper can significantly reduce the fatigue crack growth rate and extend paper's high cycle fatigue life. Lastly, from the strain fields of tearing specimens, I was able to characterize paper's crack tip process zone and the zone of active plasticity (ZAP) whose shape depended on the orientation of the fiber network. Although paper has a completely different structure and failure mechanism from metals, I found that tearing of paper also followed a steady-state process, which was previously observed in thin sheet aluminum foils.