There is now a CONTENT FREEZE for Mercury while we switch to a new platform. It began on Friday, March 10 at 6pm and will end on Wednesday, March 15 at noon. No new content can be created during this time, but all material in the system as of the beginning of the freeze will be migrated to the new platform, including users and groups. Functionally the new site is identical to the old one. webteam@gatech.edu
*********************************
THE SCHOOL OF MATERIALS SCIENCE AND ENGINEERING
GEORGIA INSTITUTE OF TECHNOLOGY
Under the provisions of the regulations for the degree
MASTER OF SCIENCE
on Monday, April 9, 2018
2:30 PM
in LOVE 210
will be held the
MASTER’S THESIS DEFENSE
for
Christopher Arnold
“The Synthesis of Atomically Thin Pt Monolayer to Multilayer Pt Films on Graphene and MoS2”
Committee Members:
Prof. Faisal Alamgir, Advisor, MSE
Prof. Matthew McDowell, MSE
Prof. Antonia Antoniou, ME
Abstract:
In the area of catalysis, substantial research is aimed at exploring the influence of the size and morphology of precious metal nanoparticles as well as catalyst supports on reaction kinetics. Recently, this has evolved into depositing highly wetted monolayers/multilayers (ML) of precious metal onto various catalyst supports. Similar to nanoparticles, ML growth significantly reduces precious metal loading (therefore improving cost) but additionally enhances catalytic activity with a better surface area to mass ratio and encouraging the substrate to tune the catalyst’s electronic properties via ligand effects and strained lattice geometry.
This work explores the deposition of Pt-ML on graphene in full 3D and 2D MoS2 as well as the influence of the Ni substrate ligand effect in electrocatalysis. Commercially available, Ni foam was utilized as a substrate for the 3D graphene growth before Pt was deposited layer-by-layer in a surface-limited electrochemical scheme to achieve highly wetted and atomically thin growth. A similar surface-limited technique was utilized for the deposition of Pt on both vertically and horizontally aligned MoS2. High resolution TEM, XPS, SEM/EDX, and electroanalytical techniques were used to characterize these samples and reveal the evolution of the atomic/electronic structure as a function of Pt-ML thickness. It is demonstrated that the synthesis scheme outlined here allows for the design of dimensionally-controlled and ligand-flexible catalyst architectures that can have a wide range of chemical applications.