There is now a CONTENT FREEZE for Mercury while we switch to a new platform. It began on Friday, March 10 at 6pm and will end on Wednesday, March 15 at noon. No new content can be created during this time, but all material in the system as of the beginning of the freeze will be migrated to the new platform, including users and groups. Functionally the new site is identical to the old one. webteam@gatech.edu
*********************************
THE SCHOOL OF MATERIALS SCIENCE AND ENGINEERING
GEORGIA INSTITUTE OF TECHNOLOGY
Under the provisions of the regulations for the degree
DOCTOR OF PHILOSOPHY
on Monday, December 19, 2016
3:00 PM
in MRDC 3515
will be held the
DISSERTATION PROPOSAL DEFENSE
for
Anirudh Ramanujapuram
"Degradation mechanisms of electrodes in high voltage aqueous lithium-ion batteries"
Committee Members:
Prof. Gleb Yushin, Advisor, MSE
Prof. Faisal Alamgir, MSE
Prof. Preet Singh, MSE
Prof. Matthew McDowell, ME
Prof. Marta Hatzell, ME
Abstract:
Lithium-ion batteries are the most popular energy devices for almost all equipment today. From cell-phones and laptops, to advanced uses in automotive and aircraft applications, lithium-ion batteries have slowly taken over the market. Unfortunately, today’s lithium-ion batteries are also highly unsafe. They rely heavily on organic solvents for electrolytes in the battery. These organic solvents are inherently flammable in nature and have caused several fires reported in batteries over the past few years.
In this research, we aim to replace this flammable liquid with a safer alternative such as water. Water-based batteries offer greatly improved safety and much lower cost (from lower raw material cost to open air manufacturing). In addition, water based electrolytes have faster ionic mobility for lithium ions and thus can be potentially used for much faster charging batteries or batteries with thicker electrodes.
We will discuss the electrochemical performance characteristics and stability of LCO in as a cathode in aqueous electrolytes. While LCO has been demonstrated to cycle for 20-100 cycles in aqueous environments the causes of its degradation have not been investigated in detail. Our studies demonstrated that LCO cathodes with remarkably stable performance showing only 13 % fading after over 1500 cycles. Post mortem analysis of the electrodes was conducted to understand the effect of cycling and the causes of degradation. Electrolyte composition was found to have a dramatic impact on the electrochemical performance and stability of LCO in aqueous environments.
Current work focuses on understanding the performance and degradation mechanism of titanium dioxide (TiO2 – anatase) in high concentration aqueous electrolytes. Literature has shown that TiO2 can be cycled in TiO2 at high rates, but the fundamental understanding of why TiO2 degrades in aqueous electrolytes is still unknown.